Nghiên cứu tính chất cấu trúc của que nano ZnO

Nguyễn Trí Tuấn * , Vũ Thị Hằng và Nguyễn Trọng Tuân

* Tác giả liên hệ (trituan@ctu.edu.vn)

Article Sidebar

Full Text: PDF

Ngày nhận bài: 20-04-2021
Ngày duyệt đăng: 25-02-2016
Ngày xuất bản: 06-06-2016
Title: Studies on structure properties of ZnO nanorods
DOI: 10.22144/ctu.jvn.2016.053
Lượt xem
137
Downloads
98
Crossref
Scopus
Google Scholar
Europe PMC
Trích dẫn
Tuấn, N. T., Hằng, V. T., & Tuân, N. T. (2016). Nghiên cứu tính chất cấu trúc của que nano ZnO. Tạp chí Khoa học Đại học Cần Thơ, (42), 91-96. https://doi.org/10.22144/ctu.jvn.2016.053
Số báo
Số. 42 (2016)
Chuyên mục
Tự nhiên

Abstract

ZnO nanorods with the average size of 60 nm×450 nm were successfully fabricated by hydrothermal synthesis method in the presence of ZnCl2 and NH3 solution as the starting materials at 190-230oC for 20 hours. The powder samples was characterized by means of X-ray powder diffraction (XRD), Field Emission Scan Electron Microscopy (FESEM) and Energy-Dispersive X-ray spectroscopy (EDX). The photoluminescence (PL) properties of the sample were investigated. Some factors affecting the morphologies and optical properties were also studied.
Keywords: ZnO nanorods, Hydrothermal synthesis

Tóm tắt

Que nano có kích thước trung bình 60 nm x 450 nm, được chế tạo thành công bằng phương pháp thủy nhiệt, với chất ban đầu là ZnCl2 và NH3 và que nano ZnO được hình thành ở nhiệt độ 190-230 oC trong 20 h. Mẫu bột chế tạo được đem đi đo nhiễu xạ tia X (XRD), ảnh hiển vi điện tử quét phát xạ trường và phổ năng lượng tán xạ tia X (EDX). Tính chất huỳnh quang của mẫu đã được khảo sát. Một vài thông số ảnh hưởng đến hình thái học và tính chất quang cũng được nghiên cứu.
Từ khóa: Que nano ZnO, tổng hợp thủy nhiệt

Article Details

Tài liệu tham khảo

Hanmei Hu, Xianhuai Huang, Chonghai Deng, Xiangying Chen, Yitai Qian, 2007. Hydrothermal synthesis of ZnO nanowires and nanobelts on a large scale, Materials Chemistry and Physics, 106: 58 - 62.

Huiying Wei, Youshi Wu, Ning Lun, Chunxia Hu, 2005. Hydrothermal synthesis and characterization of ZnO nanorods, Materials Science and Engineering A, 393: 80 – 82.

Jing Chen, Wei Lei, Weiqiang Chai, Zichen Zhang, Chi Li, Xiaobing Zhang, 2008. High field emission enhancement of ZnO-nanorods via hydrothermal synthesis, Solid-State Electronics, 52: 294 - 298.

Jinmin Wang, Lian Gao, 2004. Hydrothermal synthesis and photoluminescence properties of ZnO nanowires, Solid State Communications, 132: 269 - 271.

L.Z. Pei, H.S. Zhao, W. Tan, H.Y. Yu, Y.W. Chen, Qian-Feng Zhang, 2009. Hydrothermal oxidization preparation of ZnO nanorods on zinc substrate, Materials characterization, 60: 1063 - 1067.

Mingsong Wang, Yajun Zhou, Yiping Zhang, Eui Jung Kim, Sung Hong Hahn and Seung Gie Seong, 2012. Near-infrared photoluminescence from ZnO,Applied Physics letters, 100: 101906.

Xiangyang Ma, Hui Zhang, Yujie Ji, Jin Xu, Deren Yang, 2005. Sequential occurrence of ZnO nanopaticles, nanorods, and nanotips during hydrothermal process in a dilute aqueous solution, Materials Letters, 59: 3393 -3397.

Xiuping Jiang, Youzhi Liu, Yanyang Gao, Xuejun Zhang, Lihong Shi, 2010. Preparation of one-dimensional nanostructured ZnO, Particuology, 8: 383-385.

Y.Xi, C.G. Hu, X.Y. Han, Y.F. Xiong, P.X. Gao, G.B. Liu, 2007. Hydrothermal synthesis of ZnO nanobelts and gas sensitivity property, Solid State Communications, 141: 506 - 509.

Yong-hong Ni, Xian-wen Wei, Jian-ming Hong, Yin Ye, 2005. Hydrothermal preparation and optical properties of ZnO nanorods, Materials Science and Engineering B, 121: 42 - 47.

Zafar Hussain Ibupoto, Kimleang Khun, Martin Eriksson, Mohammad AlSalhi, Muhammad Atif, Anees Ansari and Magnus Willander, 2013. Hydrothermal Growth of Vertically Aligned ZnO Nanorods Using a Biocomposite Seed Layer of ZnO Nanoparticles, Materials, 6: 3584-3597.